| 厂家(产地)：沙伯基础(原GE) | 牌号：1000 | 加工级别：注塑级 |
| 销售方式：品牌经销 | 类型：协议料 |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 吸水率 | 平衡,73℉ | ASTM D-570 | 1.25 | % | |
| 吸水率 | 24小时，73℉ | ASTM D-570 | 0.250 | % | ||
| 熔体流动速率 | ASTM D-1238 | 8.9 | g/10min | |||
| 物理性能 | 模具收缩率 | ASTM D-955 | 5-7 | in/inE-3 | ||
| 固体比重 | ASTM D-792 | 1.27 | ||||
| 机械性能 | 挠曲模量 | ASTM D-790 | 480000 | Psi | ||
| 洛氏硬度 | ASTM D-785 | 109 | Psi | |||
| 屈服抗拉强度 | ASTM D-638 | 15200 | Psi | |||
| IZOD无缺口冲击强度 | ASTM D-4812 | 25.0 | ft-lb/in | |||
| 屈服抗拉伸长 | ASTM D-638 | 7.0 | % | |||
| 屈服挠曲强度 | ASTM D-790 | 22000 | Psi | |||
| IZOD缺口冲击强度 | ASTM D-256 | 1.0 | ft-lb/in | |||
| 泰伯磨耗量 | ASTM D-1044 | 10 | mg/1000次 | |||
| 断裂抗拉伸伸长 | ASTM D-638 | 60.0 | % | |||
| 电气性能 | 介电强度 | 62mils | ASTM D-149 | 831 | V/mil | |
| 介电常数 | 1KHz | ASTM D-150 | 3.15 | |||
| 体积电阻率 | ASTM D-257 | 1×1017 | Ω.cm | |||
| 损耗因数 | 1KHz | ASTM D-150 | 0.0012 | |||
| 热性能 | 热指数 | 电性能 | UL746B | 170 | ℃ | |
| 机械冲击性能 | UL746B | 170 | ℃ | |||
| 非机械性能 | UL746B | 170 | ℃ | |||
| 维卡软化点 | ASTM D-1525 | 426 | ℉ | |||
| 线膨胀系数 | flow | ASTM E-831 | 3 | E-5/in/in℉ | ||
| xflow | ASTM E-831 | 3 | E-5/in/in℉ | |||
| 燃烧性 | UL 94 | 5VA | class | |||
| 热变形温度 | 264Psi | ASTM D-648 | 392 | ℉ | ||
| 热变形温度 | 66Psi | ASTM D-648 | 410 | ℉ | ||
| PEI（聚醚酰亚胺） 具有突出的热力（长期耐温180℃、改性增强长期耐温210℃）、表现出良好的韧性和刚性，具有较高的硬度，较好的耐磨性能、具有突出的电性能、耐高低温并可透过微波，使之极适合用在电气/电子绝缘件方面及在高温下要求有较高强度和刚度的各种各样结构性元器件方面。 由于具有较好的抗水解性，使它在医疗器械和分析仪器领域得到广泛应用，同时作为非结晶材料由于***熔点使PEI具有良好的隔热性能。 类型：无定形 特性：高热稳定性，高强度，环境稳定性好，热膨胀系数低，与PEEK相容，抗冲击 鉴别：呈透明状，乳黄色，燃烧时有烧焦气味，火焰呈黄色 | |
推荐选择场合 | 可能面临缺陷 |
| 工作温度范围-170～180°C，耐热稳定性高； 要求制品有较高刚性和硬度,同时还具有较好的韧性; 对制品耐磨有较高要求,但不是非常苛刻; | 对模具注塑设备等要求较高,成型质量有一定难度 耐化学腐蚀性不及PTFE,不能通过SMT回流焊接测试 由于熔点高、配特定颜色比较难 |
| PEI塑料产品成功应用 矩型/圆柱型连接器、部分取代PI用于石油勘探钻井设备（耐高压、高强度）、高温隔热板、半导体支架、高压绝缘垫片、高速电机轴承、航天相机聚光圈等。 | |